A steelmaking process in which oxygen is fed into a large inclined rotating vessel through water-cooled lances, but at velocities somewhat lower than in the L.D. steel process, so that the jet does not completely or continuously penetrate the slag layer. In some respects, it is like a continuously rotating open hearth. It gives better heat utilization than the L.D. steel process but is slower.